Anycubic PETG-CF Satin Carbon Fibre Filament – Titanium Grey (1kg)
Carbon-fibre reinforced PETG | Stiffer and stronger than standard PETG | Satin finish that hides layer lines | Water and weather resistant | Requires a hardened steel nozzle
Tough, stiff parts with a premium matte finish. Anycubic PETG-CF mixes carbon fibre into PETG, giving you parts that are noticeably stiffer and stronger than regular PETG. They also have a refined satin look that hides layer lines.
Stronger, stiffer parts. Carbon fibre reinforcement makes prints more rigid, so brackets, mounts, enclosures and functional parts flex less and hold their shape under load.
Satin finish that hides layer lines. The carbon fibre gives a smooth satin texture with a subtle sheen and helps disguise layer lines. Prints look clean and professional with no sanding or painting.
Built for real-world use. PETG-CF resists water and weather and handles more heat than PLA, softening at about 74°C compared with roughly 52°C for PLA. It’s a good choice for car interior parts, garden and garage fittings, and functional prototypes.
Multicolour system ready. It’s compatible with the Anycubic ACE system, and the spool is reusable.
Key features
- Carbon-fibre reinforced PETG for extra stiffness and strength
- Satin finish that hides layer lines
- Water and weather resistant
- Higher heat resistance than PLA (softens at about 74°C)
- Anycubic ACE compatible
- Reusable spool
- Requires a hardened steel nozzle, 0.4mm or larger
Specifications
- Material: PETG-CF (carbon-fibre reinforced PETG)
- Colour: titanium grey
- Net weight: 1kg
- Nozzle: hardened steel, 0.4mm or larger (required)
- Printing temperature: 240–270°C
- Bed temperature: 65–70°C
- Recommended print speed: 40–250mm/s
- Max flow rate: 11mm³/s
- Drying: required before use, 60–65°C for 6–8 hours
- Density: 1.32 g/cm³
- Melt index: 14.1 ± 1.6 g/10 min (190°C / 2.16kg)
- Melting point: 221°C
- Vicat softening temperature: 74°C
- Heat deflection temperature: 67°C (0.45 MPa)
- Water absorption (saturated): 0.38%
- Tensile strength: 54 ± 2 MPa (X-Y), 37 ± 3 MPa (Z)
- Young’s modulus: 2,550 ± 100 MPa
- Elongation at break: 12 ± 1%
- Flexural strength: 88 ± 2 MPa
- Flexural modulus: 3,100 ± 150 MPa
- Izod impact strength (X-Y): 60 ± 4 kJ/m²
- ACE compatible: yes
- Reusable spool: yes
Tips for best results
-
Use a hardened steel nozzle. Carbon fibre is abrasive and will quickly wear out a standard brass nozzle.
-
Dry the spool before printing, at 60–65°C for 6–8 hours. Damp PETG strings badly and prints weak.
- Store it sealed with desiccant between prints.
What’s in the box
- 1 × Anycubic PETG-CF Satin Carbon Fibre Filament – Titanium Grey (1kg spool)